+0086-574-89017168
Call Us 
fuchun@fu-chun.com
Send me an inquiry
9:00-18:00
Monday - Friday
AUTOMOBILE NEWS
You are here: Home » News » AUTOMOBILE NEWS
  • With the introduction of hybrid, full electric, and even hydrogen vehicles, our vehicles will continue to get more compleThat trend doesn’t seem to be slowing down anytime soon. Like all other aspects of life, the processes in the automobile industry have been changed drastically through this development.Limited to the category of cars, sometimes you can see the grade of a car at a glance. Why does it make such a big difference in appearance? Does exquisite appearance of a car add a lot of cost?

    2019.04.12

    Read More
  • In today's automobile market, the thickness of automobile body produced by major brand manufacturers is different. You may associate Japanese cars with thinner bodywork and German cars with thicker bodywork. This statement has been widely circulated on the Internet and has long been the impression of these two systems.

    2018.12.05

    Read More
  • In recent years, the processing industry of axle parts in our country has developed rapidly, and various large-scale machinery processing factories are constantly innovating and improving the processing technology of axle parts. For the processing of axle parts, what technological requirements shoul

    2018.11.14

    Read More
  • Automotive hub is an important part of automotive parts. With the growth of China's automotive parts industry, the hub industry has gradually developed and expanded.Hubs on the market can be divided into steel hubs and alloy hubs according to their materials, each with advantages and disadvantages.

    2018.11.11

    Read More

Products

FAQS

  • What is 'multiple certification'?

    This is where a batch of steel meets more than one specification or grade. It is a way of allowing melting shops to produce stainless steel more efficiently by restricting the number of different types of steel. The chemical composition and mechanical properties of the steel can meet more than one grade within the same standard or across a number of standards. This also allows stockholders to minimise stock levels.

    For example, it is common for 1.4401 and 1.4404 (316 and 316L) to be dual certified - that is the carbon content is less than 0.030%. Steel certified to both European and US standards is also common.

  • What surface finishes are available on stainless steels?

    There are many different types of surface finish on stainless steel. Some of these originate from the mill but many are applied later during processing, for example polished, brushed, blasted, etched and coloured finishes.

    The importance of surface finish in determining the corrosion resistance of the stainless steel surface cannot be overemphasised. A rough surface finish can effectively lower the corrosion resistance to that of a lower grade of stainless steel.

  • Can I use stainless steel at high temperatures?

    Various types of stainless steel are used across the whole temperature range from ambient to 1100 deg C. The choice of grade depends on several factors:

    1. Maximum temperature of operation
    2. Time at temperature, cyclic nature of process
    3. Type of atmosphere, oxidising , reducing, sulphidising, carburising.
    4. Strength requirement

    In the European standards, a distinction is made between stainless steels and heat-resisting steels. However, this distinction is often blurred and it is useful to consider them as one range of steels.

    Increasing amounts of Chromium and silicon impart greater oxidation resistance. Increasing amounts of Nickel impart greater carburisation resistance.

  • Can I use stainless steel at low temperatures?

    Austenitic stainless steels are extensively used for service down to as low as liquid helium temperature (-269 deg C). This is largely due to the lack of a clearly defined transition from ductile to brittle fracture in impact toughness testing.

    Toughness is measured by impacting a small sample with a swinging hammer. The distance which the hammer swings after impact is a measure of the toughness. The shorter the distance, the tougher the steel as the energy of the hammer is absorbed by the sample. Toughness is measured in Joules (J). Minimum values of toughness are specified for different applications. A value of 40 J is regarded as reasonable for most service conditions.

    Steels with ferritic or martensitic structures show a sudden change from ductile (safe) to brittle (unsafe) fracture over a small temperature difference. Even the best of these steels show this behaviour at temperatures higher than -100 deg C and in many cases only just below zero.

    In contrast austenitic steels only show a gradual fall in the impact toughness value and are still well above 100 J at -196 deg C.

    Another factor in affecting the choice of steel at low temperature is the ability to resist transformation from austenite to martensite. 

  • Is stainless steel non-magnetic?

    It is commonly stated that “stainless steel is non-magnetic”. This is not strictly true and the real situation is rather more complicated. The degree of magnetic response or magnetic permeability is derived from the microstructure of the steel. A totally non-magnetic material has a relative magnetic permeability of 1. Austenitic structures are totally non-magnetic and so a 100% austenitic stainless steel would have a permeability of 1. In practice this is not achieved. There is always a small amount of ferrite and/or martensite in the steel and so permeability values are always above 1. Typical values for standard austenitic stainless steels can be in the order of 1.05 – 1.1. 

    It is possible for the magnetic permeability of austenitic steels to be changed during processing. For example, cold work and welding are liable to increase the amount of martensite and ferrite respectively in the steel. A familiar example is in a stainless steel sink where the flat drainer has little magnetic response whereas the pressed bowl has a higher response due to the formation of martensite particularly in the corners.

    In practical terms, austenitic stainless steels are used for “non-magnetic” applications, for example magnetic resonance imaging (MRI). In these cases, it is often necessary to agree a maximum magnetic permeability between customer and supplier. It can be as low as 1.004.

    Martensitic, ferritic, duplex and precipitation hardening steels are magnetic.